DUPLEX & SUPER DUPLEX STEEL

Super Duplex Stainless Steel – F55 / S32760 / 1.4501


Bar Specifications
Uns Type Ams Astm Federal Characteristics
S32760 Super Duplex - A-276
A-314
A-479
- Similar to 32750 with slight differences, competes strongly with super austenitic grades.

1.4462 Duplex, Duplex Pipe SupplierSAGAR STEEL’S based manufacturing & supplier specialize in no-compromise manufacture using state of the art CNC equipment, and the finest steels available.

We are also a very large stockholder of hot work tool steels, stainless steels (440c / 1.4125 / 4125 / X105CrMo17), duplex stainless steel (ASTM A182 A276 / AISI / F51 EN / DIN (Werkstoff) 1.4462 and X2CrNiMoN22-5-3, UNS 31803 / S31803 / S32205, Afnor Z2CND22-5Az, BS318S13, SS2377, BS332C15, EN (10283) 1.4770, branded steel SAF2205, URANUS 45N, FALC223) and now Super Duplex stainless steel conforming to ASTM / AISI / F55 in round bar and plate / sheet form.

"Super" duplex grades have enhanced pitting and crevice corrosion resistance compared with the ordinary austenitic or duplex types. This is due to the further additions of chromium, molybdenum, and nitrogen to these grades. It also conforms, or is similar to, EN / DIN (Werkstoff) 4501 / 1.4501 / X2CrNiMoCuWN25.7.4 / UNS 32760 / S32760, UNS - ASTM A276 S32760 / AISI F55 / GOST 12Kh13 / Afnor Z3CND25.06Az and branded steel Zeron 100. Also 1.4410 / UNS S32550 / UNS S32750 / Z3CNDU25.07Az / SS2328 / X2CrNiMoCuN25.6.3 / SAF 2507 SANMAC / Uranus 52N.


Corresponding Standards:
EN/DIN 1.4501
X2CrNiMoCuWN25.7.4
AFNOR Z3CND25.06Az
UNS S32760
AISI F55 (A182 / A276 / A479)
GOST 12Kh13
BRANDS® ZERON100a
NORSOK M630 MDS D57 BAR M630 MDS D54 FORGINGS M630 MDS D55 PLATE M630 MDS D56 CASTINGS M650 Qualification of Manufacturer
OTHER NACE MR01-75 ISO 15156 EN 10088-3 PED 97/23/EC ASTM G48 Method A ASTM A751 COMPOSITION ASTM A388 U/T API 6A - PSL 4



Chemical Composition
UNS S32760

C Si Mn P S Ni Cr Mo N Cu W PRE*
Min 6 24 3 0.2 0.5 0.5 40
Max 0.03 1 1 0.03 0.01 8 26 4 0.3 1 1


Industries that use 32760 include:

•Chemical
•Desalination
•Flue gas desulfurization
•Marine
•Metallurgical
•Mining
•Oil and Gas
•Pharmaceutical
•Pollution control
•Power generation
•Pulp and Paper

Products partially or completely constructed of 32760 include:
•Absorber towers
•Cargo tanks
•Chemical tankers
•Ducting
•Engineering equipment for pollution control
•Fans
•Heat exchangers
•Manifolds
•Piping
•Pressure vessels •Risers
•Rotors
•Seawater, firewater and subsea pipe work systems
•Utility and industrial scrubber systems
•Valves
The information above is not warranted, guaranteed, or for design purposes.



Super Duplex stainless steel - F53 / S32750 / 1.4410


Corresponding Standards:

EN/DIN 1.44 X2CrNiMoN25.7.4
AFNOR Z3CND25.07Az
UNS S32750
AISI F53 (A182 / A479)
SS 2328
BRANDS® URANUS 47N(+)


Similar to:
UNS S32550 / S32520 / FERRALIUM 255-SD50 / S31260 / S39226
UNS S32760 / AISI-F55 / 1.4501
Z3CNDU25.07Az / Z3CND25.06Az
X2CrNiMoCuN25.6.3 / X2CrNiMoCuWN25.7.4
1.4507 / 1.4501
ZERON 100® URANUS52N(+)®
GOST 12Kh13


Chemistry Analysis
C MN P S SI CR NI MO CU OTHER M/NM
0.03 1.2 0.35 0.02 0.08 24.-26. 6. – 8. 3. – 5. 0.5 N .24 – .32 INQUIRE


Bar Specifications
Uns Type Ams Astm Federal Characteristics
S32750 Super Duplex - A-479 - Higher chromium and nitrogen content in Super Duplex makes it superior in corrosion resistance and enables a longer lifespan than Duplex.

Industries that use Super Duplex include:
•Chemical
•Marine
•Oil and Gas production
•Petrochemical
•Power
•Pulp and Paper
•Water desalinization

Products partially or completely constructed of Super Duplex include:
•Cargo tanks
•Fans
•Fittings
•Heat exchangers
•Hot water tanks
•Hydraulic piping
•Lifting and pulley equipment
•Propellers
•Rotors
•Shafts
•Spiral wound gaskets
•Storage vessels
•Water heaters
•Wire



Duplex stainless steel - F51 / S31803 / S32205/ 1.4462


Super Duplex Steel, Duplex 2205 In India
UNS S31803 and UNS S32205 are commonly referred to as Duplex 2205® material, whose “Duplex” name is derived from the mixed micro structure which contains about equal portions of ferrite and austenite. Developed more than 70 years ago in Sweden precisely for the sulfite paper industry where the Duplex’s were used to combat corrosion problems caused by chloride-bearing cooling waters and other aggressive chemical products. Since then there have been advancements in the composition such as the deliberate addition of nitrogen as an alloying agent, which afterwards quickly made Duplex the “workhorse” of stainless steels.

Generally, UNS S31803 has been solely designated to the Duplex 2205® grade. More recently, it has been available complying with the higher corrosion resistant composition UNS S32205. The only difference in the UNS numbers is that UNS S32205 contains a higher nitrogen content which guarantees better corrosion resistance. Composed of between 21% to 23% chromium, 4.5% to 6.5% nickel, 5% to 3.5% molybdenum, 2% manganese, and 1% silicon, with the balance being iron. Also found in Duplex Stainless Steel are trace amounts of carbon, phosphorus, sulfur and nitrogen.

Benefits of Duplex include: good weldability and workability, high resistance to corrosion fatigue, stress corrosion cracking (especially chloride stress corrosion cracking), erosion, and high energy absorption. Other advantages of Duplex are higher heat conductivity and low thermal expansion compared to austenitic stainless steels, high strength, good resistance to sulfide stress corrosion, and high resistance to pitting and crevice to corrosion. Duplex 2205® accounts for over 80% of the total usage of Duplex stainless steels throughout the world because of its superior workability as well as corrosion resistance.


Corresponding Standards:
EN/DIN 1.4462 X2CrNiMoN22.5.3
AFNOR Z2CND22.05Az
AISI - A182 F51 (329LN) / F60
UNS - ASTM A276 S31803 / S32205
BRANDS® SAF 2205 - SANMAC URANAUS 45N FALC223
SS 2377
BS (WROUGHT) 318S13
BS (CAST) 332C15
EN (10283) 1.45


Chemical Composition

C Si Mn P S Ni Cr Mo N
Min 4.5 21 2.5 0.08
Max 0.03 1 2 0.03 0.02 6.5 23 3.5 0.2


Bar Specifications
Uns Type Ams Astm Federal Characteristics
S31803/S32205 Duplex - A-276
A-479
- Roughly double the strength of standard austenitic stainless steels, designed to improve resistance in many applications such as chloride environments and sulfide stress corrosion.



Duplex Stainless Steel - SS 329 / S32900 / 1.4460


Super Dulplex SteelOne of the earliest duplex steel which is reflected in its higher permitted carbon content. Its resistance to pitting (PREN about 32) and to crevice corrosion is below that of super duplex steels, therefore use in seawater is limited. Exposure to moderate and high temperature and less rapid cooling may cause embrittlement. Accordingly, design stress values in ASME II do not extend above 260°C for S32900. Impact values are high at room temperature. However, the proportion and orientation of ferrite in welds and base material may significantly affect toughness at subzero temperatures.

UNS S32900 Chemical Composition
C(Carbon) 0.08%Max
Fe(Iron) Balance
Mn(Manganese) 1.0%Max
Si(Silicon) 0.75%Max
S(Sulphur) 0.03%Max
P(Phosphorus) 0.04%Max
Cr(Chromium) 23-28%
Ni(Nickel) 2.5-5.0%
Mo(Molybdenum) 1.0-2.0%
UNS S32900 Physical Properties
Density 7800kg/m3
Melting Range 1450-1510°C
UNS S32900 Mechanical Properties
Hardness Brinnel 230
Tensile Strength@Break 725Mpa/10500psi Min
Tensile Strength@Yiel 550Mpa/79800psi Min0.2%offset
Elongation@Break 25%Min in 2"

Duplex Stainless Steel 329 also conforms, or is similar to EN/DIN 1.4460 and 00Cr25Ni5Mo2 / SUS 329J1 / AISI 329 / UNS S32900 / Brands SS44 / SS 2324 / Din X8CrNiMo27-5 / ASME SA268 / ASTM A268 / ASTM A511 / SS 14 2324 / SIS 14 2324 / 453S

Duplex Stainless steel 329 can be used for heat exchangers, chemical tanks, refineries, shafts (marine, etc) pressure vessel parts, flanges, fittings & pipes for the oil and gas industries and offshore technology, paper industry, compressor parts and seawater desalination plants amongst many other applications.

Machining performance
Download UNS S32900 the mechanical properties of the report, the report provides detailed performance analysis and application.

Principal Design Features
One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.

Machinability
Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.

Heat Treatment
CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.

Welding
Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.

Forging
Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.